Enhanced performance of cobalt ferrite encapsulated in graphitic shell by means of AC magnetically activated catalytic wet peroxide oxidation of 4-nitrophenol

Abstract

Here we report preliminary catalytic wet peroxide oxidation (CWPO) experiments performed in the presence of an alternating current (AC) magnetic field. One ferromagnetic graphitic nanocomposite - composed by a cobalt ferrite core and a graphitic shell (CoFe2O4/MGNC), was employed in the process, here named magnetically activated catalytic wet peroxide oxidation (MA-CWPO). An aqueous solution containing 5.0 g L-1 of 4-nitrophenol (4-NP) to simulate a high strength polluted stream was used as model system. The experiments were performed at room temperature and atmospheric pressure, with stoichiometric amount of hydrogen peroxide (H2O2), pH = 3 and CoFe2O4/MGNC catalyst load = 5.0 g L-1 (corresponding to a 4-NP/CoFe2O4 mass ratio of 6.9, as CoFe2O4 accounts for 14.4 wt% of CoFe2O4/MGNC). It was shown that the performance of CWPO is enhanced upon application of an AC magnetic field (frequency of 533.9 kHz and magnitude of 240 G). As a result, high 4-NP mineralization was obtained by MA-CWPO (as reflected by a total organic carbon abatement of 79% after 4 h of reaction, instead of 39% in the absence of a magnetic field). This positive effect was ascribed to the localised increase of CoFe2O4/MGNC surface temperature resulting from heat release upon exposure of the nanoparticulated catalyst to an AC magnetic field, which accelerates the catalytic decomposition of H2O2 via hydroxyl radicals (HO center dot) formation.